Portland cement type ۱-۴۲,۵:

Because of its advance resistivity, this type of cement is one of the most popular cements in the world. It can be used for normal constructions which have no limitation of environmental conditions (e.g. water, sand and …). But, because of high temperature of hydration, the usage of the cement type ۱-۴۲,۵ is not suggested for warm area (e.g. Hormozgan Providence). There is also limitation of using this type of cement for gypseous lands or those affected by sea water, because of low strength against sulfate attacks. In spite of the mentioned limitation, Hormozgan Cement Co. has tried to reduce the environmental vulnerability of the concrete following the usage of this product.
chemical composition
(%) (%)
MIN MAX MIN MAX
Silicon Dioxide SiO۲ ۲۰٫۰۰ ۲۲٫۰۰ Insoluble Residue I.R. ۰٫۱۰ ۰٫۷۰
 Aluminium Oxide  Al۲O۳ ۴٫۶۰ ۵٫۴۰ Free Lime Free CaO ۰٫۷۰ ۱٫۴۰
Ferric Oxide   Fe۲O۳ ۳٫۵۰ ۴٫۰۰ Lime Saturation Factor LSF ۰٫۹۲ ۰٫۹۷
Calcium Oxide CaO ۶۳٫۰۰ ۶۵٫۰۰ Silica Module SiM ۲٫۴۰ ۲٫۶۰
 Magnesium Oxide MgO ۱٫۵۰ ۲٫۵۰ Alomina Module AlM ۱٫۲۰ ۱٫۵۰
Sulphur Trioxide   SO۳ ۱٫۵۰ ۲٫۵۰ Tricalcium Silicate C۳S ۵۰٫۰۰ ۶۰٫۰۰
 Potassium Oxide K۲O ۰٫۵۰ ۰٫۷۰ Dicalcium Silicate C۲S ۱۵٫۰۰ ۲۵٫۰۰
Sodium Oxide Na۲O ۰٫۳۰ ۰٫۵۰ Tricalcium Aluminate C۳A ۵٫۰۰ ۹٫۰۰
 Loss on Ignition L.O.I ۰٫۶۰ ۰٫۱۰۰ Tetracalcium Alumino Ferrite C۴AF ۱۰٫۰۰ ۱۲٫۰۰

 

physical composition
MIN MAX
Fineness Blaine test (cm۲/g) ۳۰۰۰ ۳۳۰۰
Expansion Autoclave (%) ۰٫۰۵ ۰٫۱۶
Setting time: Initial (minute) ۱۲۰ ۱۶۰
Final (minute) ۱۷۰ ۳۱۰
Compressive Strenght: After ۲ days (kg/cm۲) ۲۰۰ ۲۵۰
After ۳ days (kg/cm۲) ۲۵۰ ۳۰۰
After ۷ days (kg/cm۲) ۳۰۰ ۳۵۰
After ۲۸ days (kg/cm۲) ۴۲۵ ۵۰۰

 

LSF=۱۰۰×CaO/[(۲,۸×SiO۲)+(۱,۱۸×Al۲O۳)+(۰,۶۵×Fe۲O۳)]
C۳S=(۴,۰۷۱×CaO)-(۷,۶×SiO۲)-(۶,۷۱۸×Al۲O۳)-(۱,۴۳×Fe۲O۳)-(۲,۸۵۲×SO۳)
C۲S=(۲,۸۶۷×SiO۲)-(۰,۷۵۴×C۳S)
C۳A=(۲,۶۵×Al۲O۳)-(۱,۶۹۲×Fe۲O۳)
C۴AF=(۳,۰۴۳×Fe۲O۳